These terms are used inconsistently, especially in the context of contemporary glass. When used as a noun, murrina usually refers to a multicolored element embedded in an object, whereas murrine most often refers to slices of a complex cane.

(1) The process of founding or melting the batch; (2) heating pieces of glass in a kiln or furnace until they bond (see Casting and Kiln forming); (3) heating enameled glasses until the enamel bonds with the surface of the object.

The process of reheating a blank until it becomes soft and gradually flows under its own weight over or into a former mold and eventually assumes the shape of the mold. Soda-lime glass becomes soft at about 1110°F (600°C). Slumping is also known as sagging.

A form used for shaping and/ or decorating molten glass. Some molds (e.g., dip molds) impart a pattern to the parison, which is then withdrawn, and blown and tooled to the desired shape and size; other molds (sometimes known as full-size molds) are used to give the object its final form, with or without decoration. Dip molds consist of a single part and are usually shaped like beakers. Full-size molds usually have two or more parts and can be opened to extract the object. Nowadays, most molds are made of metal, but stone, wood, plaster, and earthenware molds were used in the past and are still occasionally employed today.

The generic name for decorative windows made of pieces of colored glass fitted into cames and set in iron frames. Strictly speaking, the term is inaccurate because, in addition to glass colored by staining, glaziers used, and continue to use, glass colored throughout by metallic oxide, glass colored by flashing, and glass decorated with enamel.

The technique of forming objects from rods and tubes of glass that, when heated in a flame, become soft and can be manipulated into the desired shape. Formerly, the source of the flame was an oil or paraffin lamp used in conjunction with foot-powered bellows; today, gas-fueled torches are used.

(1) Several types of glass with newly developed surface textures, shaded colors, or casing, made in the United States from about 1870 and in Europe between about 1880 and 1900; (2) more generally, especially when written “art glass,” any ornamental glassware made since the mid-19th century.